Development of Low-temperature Sinterable Ag Nano Paste
Successful development of Ag paste which provides specific resistance of 7.1 x 10-6Ω·cm by sintering at 120℃/30 minute drying. For wiring with this paste, screen-printing is supported.
Learn more
-
03/23/2020
Establishment of resin design method by simulation:
On the fluidity of resinsA simulation method that can analyze the behavior of resin as a fluid was developed.
At present, we are responding to the needs of engineers and customers by analyzing which resin is the best.Learn more
-
12/16/2019
Development of a nano anchoring treatment technology for a copper foil surface to provide low roughness, high adhesion, and high reliability and the copper foil prepared by the technology
Low roughness, high adhesion, and surface stabilization have been achieved by varying surface treatment agents
Learn more
-
01/15/2019
Development of a spray-coated paste for electromagnetic wave shielding
We have succeeded in developing a spray applicable conductive paste. Our newly developed paste provides a film with 5 to 6 µm upper thickness and 3 to 4 µm side thickness to our target of 10 µm or less film thickness.
Learn more
-
01/15/2019
Development of a solid-state secondary battery
We succeeded in developing an oxide-based, solid-state secondary battery with charge/discharge characteristics and good reliability test results.
Learn more
-
01/15/2018
Degradation of the front-side Ag electrodes and generation of a lead compound on silicon solar cells during a high-temperature, high-humidity test
We investigated the cause of deterioration inside solar cell modules. Recipient of the Best Poster Award at the 7th World Conference on Photovoltaic Energy Conversion (WCPEC-7), 2018 in collaboration with the Fukushima Renewable Energy Institute, AIST (FREA) of National Institute of Advanced Industrial Science and Technology (AIST).